Strukturbericht
designation
Prototype
Space group
A-compounds
A1
Cu
Fm
3
m
A2
W
Im
3
m
A3
Mg
P6
3
/mmc
A3'
α-La
P6
3
/mmc
A4
C (diamond)
Fd
3
m
A5
β-Sn
I4
1
/amd
A6
Indium
I4/mmm
A7
α-As
R
3
m
A8
gray Se
P3
1
21
A9
C (graphite)
P6
3
/mmc
A10
P (white)
P4
1
32
A12
α-Mn
I
4
3m
A13
β-Mn
P4
1
32
A14
I
2
Cmca
A15
β-W
Pm
3
n
A16
α-S
Fddd
A17
P (black)
Cmca
A
a
α-Pa
I4/mmm
A
b
β-U
P4
2
/mnm
A
c
α-Np
Pnma
A
d
β-Np
P4/nmm
A
f
γ-HgSn
6-10
P6/mmm
A
g
B
P4
2
/nnm
A
h
α-Po
Pm
3
m
A
i
β-Po
R
3
m
A
k
γ-monoclinic Se
P2
1
/c
A
l
β-monoclinic Se
P2
1
/c
B-compounds
B1
NaCl
Fm
3
m
B2
CsCl
Pm
3
m
B3
ZnS
F
4
3m
B4
ZnS
P6
3
mc
B8
1
NiAs
P6
3
/mmc
B8
2
Ni
2
In
P6
3
/mmc
B9
α-HgS
P3
2
21
B10
PbO
P4/nmm
B11
γ-CuTi
P4/nmm
B13
β-NiS
R3m
B16
GeS
Pnma
B17
PtS
P4
2
/mmc
B18
CuS
P6
3
/mmc
B19
β'-AuCd
Pmma
B20
FeS
P2
1
3
B21
α-CO
P2
1
3
B26
CuO
C2/c
B27
FeB
Pnma
B32
NaTl
Fd
3
m
B33
CrB
Cmcm
B34
PdS
P4
2
/m
B35
CoSn
P6/mmm
B37
SeTl
I4/mcm
B
a
CoU
I2
1
3
B
b
ζ-AgZn
P
3
B
e
CdSb
Pbca
B
g
MoB
I4
1
/amd
B
h
WC
P
6
m2
B
i
AsTi
P6
3
/mmc
B
k
BN
P6
3
/mmc
C-compounds
C1
CaF
2
Fm
3
m
C2
FeS
2
Pa
3
C3
Cu
2
O
Pn
3
m
C4
TiO
2
P4
2
/mnm
C5
TiO
2
I4
1
/amd
C6
CdI
2
P
3
m1
C7
MoS
2
P6
3
/mmc
C8
β-SiO
2
P6
2
22
C9
β-Cristobalite
Fd
3
m
C10
β-Tridymite
P6
3
/mmc
C11
a
CaC
2
I4/mmm
C11
b
MoSi
2
I4/mmm
C14
MgZn
2
P6
3
/mmc
C15
MgCu
2
Fd
3
m
C16
CuAl
2
I4/mcm
C18
FeS
2
Pnnm
C19
α-Sm
R
3
m
C21
TiO
2
Pbca
C22
Fe
2
P
P
6
2m
C23
PbCl
2
Pnma
C24
HgBr
2
Cmc2
1
C25
HgCl
2
Pnma
C27
CdI
2
P6
3
mc
C32
AlB
2
P6/mmm
C33
Bi
2
Te
3
R
3
m
C35
CaCl
2
Pnnm
C36
MgNi
2
P6
3
/mmc
C37
Co
2
Si
Pnma
C38
Cu
2
Sb
P4/nmm
C40
CrSi
2
P6
2
22
C42
S
2
Si
Ibam
C43
ZrO
2
P2
1
/c
C44
GeS
2
Fdd2
C46
AuTe
2
Pma2
C47
SeO
2
P4
2
/mbc
C49
ZrSi
2
Cmcm
C50
PdCl
2
Pnmn
C54
TiSi
2
Fddd
D-compounds
D0
2
CoAs
3
Im
3
D0
3
BiF
3
Fm
3
m
D0
4
CrCl
3
P3
1
12
D0
5
BiI
3
R
3
D0
6
LaF
3
P
3
c1
D0
9
α-ReO
3
Pm
3
m
D0
11
Fe
3
C
Pnma
D0
12
AlF
3
R32
D0
15
AlCl
3
C2/m
D0
17
BaS
3
P
4
2
1
m
D0
18
Na
3
As
P6
3
/mmc
D0
19
Ni
3
Sn
P6
3
/mmc
D0
21
Cu
3
P
P6
3
/cm
D0
22
Al
3
Ti
I4/mmm
D0
23
Al
3
Zr
I4/mmm
D0
24
Ni
3
Ti
P6
3
/mmc
D5
1
Al
2
O
3
R-3c
E-compounds
E1
1
CuFeS
2
I
4
2d
E1
b
AgAuTe
4
P2/c
E2
1
CaTiO
3
Pm
3
m
E2
2
FeTiO
3
R
3
F-compounds
F0
1
NiSSb
P2
1
3
G-compounds
G0
1
CaCO
3
R
3
c
H-compounds
H1
1
Al
2
MgO
4
Fd
3
m
to be continued...
main data sources:
Crystal Lattice Structures Webpage
,
Wikipedia Strukturbericht designation
,
Crystallography Open Database
,
Steffen Weber's Structure Type gallery